所報 107

13/46

In this experimental study on the reiteration frost and wheel running combined damaged of the RC slabs. And damaged investigation of cause were the water and cement ratio (W/C). All results obtained by the Load carrying wheel tracking machine and result from the equivalent number of cycles and S/N curve. As the results, 57 percent W/C slabs specimens fatigue resistance had decreased 54 percent and decrease static elastic modulus was 23 percent, in another 50 percent W/C slabs specimens had decreased 50 percent of number of cycles and static elastic modulus was decrease 16 percent. Those specimens were compared to no damaged RC slabs. In snow and cold region RC slabs were effective improved of fatigue and frost deterioration by the W/C ratio.Keywords : Running fatigue, Frost damage, Water-cement ratio, Deterioration damage, Fatigue resistant, Dynamic modulus of elasticityKazuhiko MINAKUCHI, Tadashi ABE and Shohei SUGURO　本研究は，輪荷重走行による疲労と凍害の複合劣化を受けたRC部材の水セメント比（W/C）の違いが耐疲労性に及ぼす影響について実験より検証したものである。その結果，輪荷重走行と凍害による複合劣化を受けた場合，乾燥状態での等価走行回数に比して，水セメント比57％、50％の供試体でそれぞれ54％，50％の低下が見られた。また，動弾性係数では乾燥状態の供試体に比して23％，16％低下している。劣化診断では，輪荷重走行と凍結・融解における融解時の湿潤状態によりセメント成分の溶出が多くスケーリングに至ることから，水セメント比を小さくすることで劣化の進行を抑制できることを明らかにした。キーワード：走行疲労、凍害、水セメント比、劣化損傷、耐疲労性、動弾性係数Journal（掲載誌）Cement Science and Concrete Technology, Vol.70, pp.421-427. 2017.－　　－11輪荷重走行による疲労と凍害の複合劣化を受けたRC部材の耐疲労性評価Evaluation of Fatigue Resistance of RC Member under Compound Deteriorationfor Running Fatigue and Frost DamagePublished Paper